Email:shbxg@shstainless.com
Email:shbxg@shstainless.com 

Grades

430

304/304L

316

316/316L

310/310S

321

Contact Us

Country/Region : China
Address:Huitong Logistics Park,Liaocheng Development Zone
Tel: 86-0635-8702133
Fax: 86-0635-8702132
mobile number :0086-13020599533
wechat:13020599533
contact person:Alice
Email:shbxg@shstainless.com
wechat:13020599533
branch office:
Xi'an Avisen Import and Export Company Limited
Tel: 86-0635-8702132
adress:No. 155 Floor 6, Block B, Building 1, No. 99 Gangwu Avenue, International Trade & Logistics Park, Xi'an, Shaanxi, China
You are here: Home » Grades » 310/310S

310/310S

Grade 310, combining excellent high temperature properties with good ductility andweldability, is designed for high temperature service. It resists oxidation incontinuous service at temperatures up to 1150°C provided reducing sulphur gases are not present. It is also used for intermittent service at temperatures up to 1040 ° C.
Grade 310S (UNS S31008) is used when the application environment involves moist corrodents in a temperature range lower than that which is normally considered "hightemperature" service. The lower carbon content of 310S does reduce its high temperature strength compared to 310.
Like other austenitic grades these have excellent toughness, even down to cryogenic temperatures, although other grades are normally used in this environment.
Grade 310L (and proprietary versions of this grade), is a 0.03% maximum carbon version of 310, sometimes used for very specific corrosive environments, such as ureaproduction.

Chemical Formula
Fe C Cr Ni  Mn Si P
<0.25% 24-26% 19-22% <2% <1.5% <0.45% <0.3%

Composition
Typical compositional ranges for grade 310 stainless steels are given in table 1.
Table 1.  Composition ranges for 310 grade stainless steel
Grade Tensile Strength
 (MPa) min		 Yield Strength 0.2% Proof
 (MPa) min		 Elongation 
(% in 50mm) min		 Hardness  
Rockwell B (HR B) 
max		 Brinell (HB)  
max
310 515 205 40 95 217  
310S 515 205 40 95 217  

Mechanical Properties
Typical mechanical properties for grade 310 stainless steels are given in table 2.
Table 2.  Mechanical properties of 310 grade stainless steel
Grade Tensile Strength
 (MPa) min		 Yield Strength 0.2% Proof
 (MPa) min		 Elongation
 (% in 50mm) min		 Hardness  
        Rockwell B (HR B) max Brinell (HB)                    
max
310 515 205 40 95 217  
310S 515 205 40 95 217  

Physical Properties
Typical physical properties for annealed grade 310 stainless steels are given in table 3.
Table 3.  Physical properties of 310 grade stainless steel in the annealed condition
Grade Density 
(kg/m3)		 Elastic Modulus 
(GPa)		 Mean Coefficient of Thermal Expansion
 (μm/m/°C)		 Thermal Conductivity
(W/m.K)		 Specific Heat 0-100°C (J/kg.K) Electrical Resistivity
 (nΩ.m)
      0-100°C 0-315°C 0-538°C at 100°C at 500°C    
310/S 7750 200 15.9 16.2 17 14.2 18.7 500 720
    
Grade Specification Comparison
Approximate grade comparisons for 310 stainless steels are given in table 4.
Table 4.  Grade specifications for 310 grade stainless steel
Grade UNS No Old British Euronorm Swedish SS Japanese JIS
    BS En No Name    
310 S31000 310S24 - 1.484 X15CrNi25-20 - SUH 310
310S S31008 310S16 - 1.4845 X8CrNi25-21 2361 SUS 310S


Applications:
Typical applications include:
• Furnace parts
• Oil burner parts
• Carburising boxes
• Heat Treatment baskets and jigs
• Heat Exchangers
• Welding filler wire and electrodes